سال انتشار: ۱۳۹۳

محل انتشار: پانزدهمین کنگره ملی مهندسی شیمی ایران

تعداد صفحات: ۷

نویسنده(ها):

s hakim – iran polymer and petrochemical institute p.o.box:14965/115
m nekoomanesh – iran polymer and petrochemical institute p.o.box:14965/115
a shahrokhinia – iran polymer and petrochemical institute p.o.box:14965/115

چکیده:

Homopolypropylene samples with an industrial Ziegler-Natta catalyst and in the presence of combined external donors, namely cyclohexyldimethoxymethylsilane (donor C) and Dicyclopenthyldimethoxysilane (donor D) with different molar ratio of donor C to D (0.3 for sample 1, 1.2 for sample 2, 4.6 for sample 3) were synthesized. A synergistic effect on molecular weight and approximately on poly dispersity index and melting temperature, decrease in crystallinity (%) and crystallization temperature from sample 1 to 3 were observed. The SSAresults showed that in spite of close average stereo-regularity, the stereo-defect distribution differences between the all of samples were so vast and from sample 1 to 3, thick lamellar amount was changed drastically and stereo-defect distribution became narrower. With using mixed external donors, different properties like high molecular weight, broad PDI and narrow stereo- defect distribution in sample 3 and low molecular weight, narrow PDI and broad stereo-defect distribution in sample 1 were obtained.